15-5PH 1.4545 Stainless Steel Bar
15-5PH 1.4545 Stainless Steel Bar
Model
15-5PH

Item specifics

Delivery condition
harden
Surface Condition
Smooth
Shape
round
Application
Aircraft components High pressure corrosive fabricated parts such as valves Shafts Fasteners Fittings and gears

Review

Description

Introduction of 15-5PH stainless:

15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.

15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in the aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.

Applications of 15-5PH stainless:

Aircraft components
High pressure corrosive fabricated parts such as valves
Shafts
Fasteners
Fittings and gears

Quality Standard of 15-5PH stainless:

ASTM A564 2004 Standard Specification for Hot Rolled and Cold Finished Age Hardening Stainless Steel Bars and Shapes
ASTM A705 Standard Specification for Age Hardening Stainless Steel Forgings

All Grades Comparison of 15-5PH stainless:

DIN

ASTM

UNS

CNU

1.4545

XM-12

S15500

15-5PH

Chemical Composition of 15-5PH stainless(%)

C

Si

Mn

P

S

Cr

Ni

Cu

Nb+Ta

0.07 max

1.0 max

1.0 max

0.030 max

0.035 max

14.0-15.0

3.5-5.5

2.5-4.5

0.15-0.45

Mechanical Properties of 15-5PH stainless:

Delivery Condition

Modulus of Elasticity(GPa)

Modulus of Rigidity(GPa)

Tensile Strength Rm (Mpa)

Yield Strength Rp0.2 (Mpa)

Elongation % in 2″ (50.8 mm)

Reduction Of Area (%)

Hardness (HRC)

A(annealed)

/

/

/

/

/

/

35 max

H 900

197.6

77.3

1378 min

1276 min

14 min

50 min

44 min

H925

/

/

1309 min

1207 min

14 min

54 min

42 min

H1025

/

75.9

1173 min

1138 min

15 min

56 min

38 min

H1075

/

69

1138 min

1035 min

16 min

58 min

36 min

H1100

/

/

1035 min

931 min

17 min

58 min

34 min

H1150

/

69

1000 min

862 min

19 min

60 min

33 min

15-5ph steel