6150 Oil Hardened and Tempered Spring Steel Wires
- Model
- 6150
Item specifics
- Diameter
- 10-40mm
- Delivery Condition
- Oil Hardened and Tempered
- Surface Condition
- Black suface,Blasted
Review
Description
Products Details:
1 High yield ratio, small spring residual deformation.
2 Stable performance: the difference of tensile strength in same coil is less than 60Mpa,which can extend the spring fatigue life.
3 The product rate after winding is high,which can reduce the cost. Oil quenching - tempering spring wire can not completely replace the cold-drawn spring wire. Especially the small size of the spring wire. Oil Hardened and Tempered spring wire is developed for the valve spring, suspension spring in fatigue resistance. And in order to achieve the best results, it should be combined with blasted process after winding. In recent years, with the improvement of the cognition level of this kind of product, this kind of product is gradually applied to clutch spring and car rigging.
Quality Standard:
ASTM A29/A29M - 05 Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for
Chemical Composition(%):
Steel Grade | C | Si | Mn | P | S | Cr | V |
6150 | 0.48-0.53 | 0.15-0.35 | 0.70-0.90 | 0.035max | 0.040 max | 0.80-1.10 | 0.15 min. |
Mechanical Properties(Quenched and Tempered Condition)(T=20°C if not differently stated):
Steel Grade | Tensile Strength Rm (Mpa) | Yield Strength Rp0.2 (Mpa) | Elongation A5 (%) | Area Reduction Ratio C (%) |
6150 | 1275 min | 1130 min | 10 min | 40 min |
Heat Treatment:
Steel Grade | Quenching Temperature (°C) | Media | Tempering Temperature (°C) |
6150 | 850 | oil | 500 |