16CrMo44 1.7337 AISI A182 F12 Hot Forged Alloy Steel Bar
16CrMo44 1.7337 AISI A182 F12 Hot Forged Alloy Steel Bar
16CrMo44 1.7337 AISI A182 F12 Hot Forged Alloy Steel Bar
16CrMo44 1.7337 AISI A182 F12 Hot Forged Alloy Steel Bar
16CrMo44 1.7337 AISI A182 F12 Hot Forged Alloy Steel Bar
Price
US $1400
Model
16CrMo44 1.7337
MOQ
1 metric ton

Item specifics

Steel grade
16CrMo44/1.7337
Applications
aerospace and oil and gas industries
Heat treatment
Normalized,Quenching and Tmenpering
Surface condition
Black or bright surface
Standard
16CrMo44/1.7337

Review

Description

Introduce

16CrMo44/1.7337  is a low-alloy steel containing chromium and molybdenum as strengthening elements.It has good mechanical property similiar like Chinese grade 15CrMo. This materail is generally used in the quenched and tempered condition.

Application

This alloy finds many applications as forgings for the aerospace and oil and gas industries, along with myriad uses in the automotive, agricultural and defense industries, Typical uses are forged gears and shafts, spindles, fixtures, jigs and collars.

Chemical component

Equivalent Grade Chemical Composition

National
Standard

Grade

C%

Si%

Mn%

Cr%

Mo%

P%

S%

DIN

16CrMo44
(1.7337)

0.13-0.2

0.15-0.35

0.5-0.8

0.9-1.2

0.4-0.5

≤0.025

≤0.035

GB

15CrMo

0.12-0.18

0.17-0.37

0.4-0.7

0.8-1.1

0.4-0.55

≤0.035

Forging

Forging of this steel should be carried out between 2200 and 1650 º F (1200 and 900 º C). The lower the finishing temperature from forging, the finer will be the grain size. This alloy should ideally not be forged below 1650 º F (900 º C) and should be slow cooled after forging.

Heat treatment

1.Nominal normalizing temperature:840-890°C

2.Hold the temperature for several hours
3.Cooling in the air


Annealing  For 16CrMo44
1.Nominal Annealing temperature:680-720°C
2.Cool slowly in the furance
3.Maximum Brinell hardness of 217

Hardening and Tempering(QT)  For 16CrMo44
1.Nominal Hardening temperature:850-870°C
2.Hold at this temperature then quench in oil or water
3.Tempering  as soon as possible when the temperature low to ambient
4.Heat uniformly to the suitable temperature of 550-640°C
5.keep the material out of the furnace ,then cool in the air


Mechanical Property( for reference only)
1.Tensile strength: 740MPa
2.Yield point: 635MPa
3.Percentage reduction of area after fracture: 50%
4.Elongation after fracture: 17%
5.Impact test (+20°C): Transverse – 27~32J; Longitud – 60~80J

Delivery Condition
1.Shape:Round/Square / Flat/Shafts/Rollers/Blocks
2.Surface condition:Black surface/Bright surface
3.Heat Treatment:Normalized/Annealed/QT
4.Straightness:Max 3mm/m(Enhanced straightness may be available on request)
5.Length:3000-5800mm suitable for 20″container.  above 6000mm,suitable for 40″ container
6.Grain Size: 5-8 acc to ASTM E112-96
7.Ultrasonic Standard: Sep1921/ASTM A388/EN 10228-3
8.Non Metallic Inclusion: 2 max acc to ASTM E45 /K4≤20 acc to DIN 50602
9.Forging Ratio: minimum 4 : 1
10.Marking: Grade/Weight/Length/Size/Heat Number


Quality Certification
A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non Metallic Inclusion
5.Heat Treatment Process
6.Grain size
7.Forging ratio
8.NDE test method/criteria

16CrMo44/1.7337 alloy steel manufacturers and suppliers,supplied with round rods,square/flat bars,rollers,shafts,blocks and forging pieces.