1.2885 X32CrMoCoV3-3-3 Hot Working Tool Steel
1.2885 X32CrMoCoV3-3-3 Hot Working Tool Steel
Model
1.2885

Item specifics

Process
hot rolled or hot forged
Delivery Condtion
annealed
Surface Condition
smooth, bright

Review

Description

1.2885 X32CrMoCoV3-3-3 H10A Hot Working Tool Steel

 

X32CrMoCoV3-3-3 1.2885 Alloy tool steel with high hardenability, high resistance to tempering, load and high hardness at elevated temperatures. The grade is distinguished by high content of Cobalt in its chemical composition.

 

Applications

Hot pressing tools exposed to severe stresses in contact with the die insert-mandrels,stamps, punching tools,dies,etc.

 

Designation by Standards

Steel No. :1.2885

DIN EN :X32CrMoCoV3-3-3

AISI :H10A

 

Chemical composition (wt.%)

C()

Si()

Mn()

P()

S()

Cr()

Mo()

V(%)

Co(%)

0.28-0.35

0.10-0.40

0.15-0.45

Max 0.030

Max 0.030

2.70-3.20

2.60-3.00

0.40-0.70

9.50-10.5

 

Mechanical properties of 1.2885, X32CrMoCoV3-3-3

Hardness in softening annealed condition <241 HB

Hardness after hardening 53.5 HRC

Hardness after tempering at temperature: 

300C = 51.5 HRC

350C = 51.5 HRC

400C = 52.0 HRC

450C = 52.5 HRC

500C = 53.0 HRC

550C = 53.5 HRC

600C = 51.5 HRC

 

Heat treatment - processes and temperatures:

Softening annealing at 740 - 770C with cooling in furnace

Relief annealing at a temperature of 600 - 700C with cooling in furnace

Nitriding at a temperature of 470 - 550C

Hardening at a temperature of 1020 - 1040C with cooling in oil

Tempering at a temperature of 500 - 600C

 