SUP12 Oil Hardened and Tempered Spring Steel Wires
- Model
- SUP 12
Item specifics
- MOQ
- 1 Metric Ton
- Quality Standard
- JIS G4801
- Delivery Condition
- Oil Hardened and Tempered
- Surface Condition
- Black suface,Blasted
- Application
- Suspension Spring,Valve Spring
- Delivery Time
- Within 30days
Review
Description
Products Details
1 High yield ratio, small spring residual deformation.
2 Stable performance: the difference of tensile strength in same coil is less than 60Mpa,which can extend the spring fatigue life.
3 The product rate after winding is high,which can reduce the cost. Oil quenching - tempering spring wire can not completely replace the cold-drawn spring wire. Especially the small size of the spring wire. Oil Hardened and Tempered spring wire is developed for the valve spring, suspension spring in fatigue resistance. And in order to achieve the best results, it should be combined with blasted process after winding. In recent years, with the improvement of the cognition level of this kind of product, this kind of product is gradually applied to clutch spring and car rigging.
Quality Standard
JIS G4801 2005 Spring Steels
Steel Grade | C | Si | Mn | P | S | Cr |
SUP 12 | 0.51-0.59 | 1.20-1.60 | 0.60-0.90 | 0.030 max | 0.030 max | 0.60-0.90 |
Mechanical Properties(Quenched and Tempered Condition)(T=20°C if not differently stated)
Steel Grade | Tensile Strength Rm (Mpa) | Yield Strength Rp0.2 (Mpa) | Elongation A5 (%) | Area Reduction Ratio C (%) |
SUP 12 | 1450-1750 | 1300 min | 6 min | 25 min |
Heat Treatment
Steel Grade | Quenching Temperature (°C) | Media | Tempering Temperature (°C) |
SUP 12 | 860 | oil | 450 |