DIN 1.7185 33MnCrB5-2 Alloy Steel Round Bars

Group Quenched and Tempered Steel Bar
Min. Order 1 piece
Terms of Payment L/C, T/T
Update Time 2019-06-03
Item specifics
Diameter50-260mm
Delivery conditionHot forged, Hot rolled, QT
Surfac conditionBlack, bright

Introduction of 1.7182 steel:

Hot rolled Hardenable Steel has been developed to be hardened, either by heat treatment after workshop processing, or by a direct hot forming & quenching process to get their final properties. Hardenable Steel is a perfect base material for a great variety of products, parts and components, that need extreme hardness, wear resistance, high strength, toughness and resistance to mechanical load. These Hardenable Steel properties after heat treatment ensure longer lifetime and considerable weight reduction. Good forming- bending- welding- and cutting properties enable the manufacturing of complicated structures, components and parts.

Application of 1.7182 steel:

Wear plates, Grader blades, Track shoes, Liner plates, Screen plates, Crushers, Knives, Saw blades, Spades, Hand tools, Ploughs, Discs for harrows, Washers, Safety parts and components

Chemical Composition of 1.7182 steel:

Grade

C

Si

Mn

P

S

Cr

B

1.7185

0.30 -0.36

0.4max

1.20- 1.50

0.025max

0.035 max

0.30- 0.60

0.0008-0.0050

Mechanical Property of 1.7182 steel:

Grade

33MnCrB5-2

Thickness

Yield

Tensile

Elongation

1.7185,33MnCrB5-2

mm

Min Mpa

Mpa

Min %

3

850

1050-1300

13

8

800

950-1200

13