DIN 1.2343 Hot Work Tool Steels

 

1.2343 Introduction:

Alloy tool steel for hot working for moulds for die casting of aluminium alloys, magnet, zinc, pressing pipes, copper alloy bars and light metals under pressure.It is characterized by very high hardenability, resistance to tempering, possibility of working at high temperatures and low susceptibility to forming a surface crack net.Disadvantages of the grade are low sensitivity to rapid temperature fluctuations during operation, low impact and shock resistance. Before use the tools must be warmed to a minimum temperature of 200 C, but must not exceed the tempering temperature.It is used for the production of hot working knives, die inserts for presses and forging machines, screws, dies, moulds for plastics, stamps, mandrels, punches, copper rolling mills.The steel is also available after ESR electroslag melting, which guarantees high purity - recommended for moulds for casting non-ferrous metal alloys under pressure, and ESF which guarantees fine-grainability.

 

The tool steel 1.2343 is a hot-work tool steel with high toughness and good heat resistance. 1.2343 is hot cracking resistant and has good thermal conductivity. For particularly difficult applications, there is this material with a special high purity ( ESU-Quality), Frequently, this material is used to manufacture extrusion. Usually 1.2343 is supplied in the soft-annealed condition.

 

1.2343 Applications:

H11 Hot Work Steels is often used for highly stressed structural parts such as aircraft landing gear. It resists softening at temperatures up to 1000 F while retaining good ductility and toughness even at strength levels on the order of 275 ksi.

 

1.2343 Quality Standard:

EN  4957 Standard Specification for Tool Steel

 

1.2343 All Grades Comparison:

ASTM

AFNOR

DIN

UNI

JIS

B.S.

H11

Z 38 CDV 5

1.2343

T20811

SKD6

BH 11

 

1.2343 Chemical Composition(%):

C

Si

Mn

P

S

Cr

V

Mo

0.33-0.43

0.80-1.25

0.20-0.60

0.030 max

0.030 max

4.75-5.50

0.30-0.60

1.10-1.60

 

1.2343 HEAT TREATMENT:

FORGING: H11 hot work steels are forged at 1121°C (2050°F). For this type of steels, forging below 899°C (1650°F) is not preferable.

ANNEALING: H11 hot work steels are annealed at 871°C (1600°F) and slowly cooled at 4°C (40°F) in the furnace.

HARDENING: Preheat to 1500 F and then heat to 1850 F and hold for 15 to 40 minutes. Air cool (air quench).

TEMPERING: Tempering is carried out on H11 tool steels at temperature ranging from 538 to 649°C (1000 to 1200°F) to obtain Rockwell C hardness of 54 to 38. Double tempering can also be performed in these steels every one hour at the preferred tempering temperature.

 

1.2343 Mechanical Properties:

Properties

Metric

Imperial

Hardness, Rockwell C (air cooled from 982°C, 45 mins)

52.5

52.5

Hardness, Rockwell C (air cooled from 1010°C, 45 mins)

56

56

Hardness, Rockwell C (air cooled from 1038°C, 45 mins)

57

57

Modulus of elasticity

207 GPa

30000 ksi

Modulus of elasticity (@538°C/1000°F)

159 GPa

23000 ksi

Modulus of elasticity (@204°C/400°F)

190 GPa

27500 ksi

Charpy impact (V-notch; air cooled from 1010°C;535°C temper temperature)

13.6 J

10.0 ft-lb

Charpy impact (V-notch; air cooled from 1010°C;650°C temper temperature)

27.1 J

20.0 ft-lb

Charpy impact (V-notch; air cooled from 1010°C;370°C temper temperature)

33.9 J

25.0 ft-lb

Machinability (1% carbon steel)

75.0 – 80.0%

75.0 – 80.0%

Poisson’s ratio

0.27-0.30

0.27-0.30

 

1.2343 Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.