EN DIN BS 1.4435 X2CrNiMo18-14-3 Bright Stainless Steel Round Bar

Model: 1.4435

Item specifics

Surface condition: Black, Blasted, Turned, Polished

Review

Description

1.4435 X2CrNiMo18-14-3 Austenitic Stainless Steel

Introduce

1.4435 is an acid-resisting austenitic CrNiMo-Steel with 18% Cr, approx. 14% Ni and at least 2.5% Mo. Due to the increased Mo-content, this material has a significantly improved corrosion resistance compared to other CrNi-Steels. 1.4435 is particularly resistant to reducing effecting organic and anorganic organic acids as well as against halogen-containing media. Furthermore, this steel is also less susceptible to pitting. The very low carbon content also improves the resistance to intergranular corrosion, allowing the use of this steel at elevated temperatures up to 450 ° C in continuous operation. 1.4435 can also be very well polished, very good deformable and can be welded excellent.

Our supply size:

Diameter : 80 to 600 mm ;

Length : 1000 to 9000 mm ;

Our advantage:

1. High Quality, Reasonable Price

2. Over 40 Years Experience

3. ISO NQA Certificated Factory

4. Worldwide shipping

5. Emergency Orders and Fast Delivery

Equivalent grades of steel X2CrNiMo18-14-3 (1.4435)

EU	USA	Germany	Japan	France	England	Italy
EN	-	DIN,WNr	JIS	AFNOR	BS	UNI
X2CrNiMo18-14-3	316L	X2CrNiMo18-14-3	SUS316L	Z3CND17-12-03	316S13	X2CrNiMo17-13

Chemical composition % of steel X2CrNiMo18-14-3 (1.4435): EN 10088-2-2005

C	Si	Mn	Ni	P	S	Cr	Mo	N
max 0.03	max 1	max 2	12.5 - 15	max 0.045	max 0.015	17 - 19	2.5 - 3	max 0.11

Equivalent grades of steel X2CrNiMo18-14-3 (1.4435)

Rm - Tensile strength (MPa) (+A)	490-700
Rm - Tensile strength (MPa) (+AT)	490-690
Rp0.2 0.2% proof strength (MPa) (+A)	190-240
Rp0.2 0.2% proof strength (MPa) (+AT)	190-200
Brinell hardness (HB): (+A)	215
Brinell hardness (HB): (+AT)	200

Application

Construction encasement, doors, windows and armatures, offshore modules, cisterns and pipes for chemical tanks, production, warehousing and over land transportation of chemicals, food and beverages, pharmacy, synthetic fibre, paper and textile plants and pressure vessels. Due to the low C-content, the resistance to intergranular corrosion is also guaranteed in the welded condition.