1.2360 X48CrMoV8-1-1 Cold Work Tool Steel
1.2360 X48CrMoV8-1-1 Cold Work Tool Steel
1.2360 X48CrMoV8-1-1 Cold Work Tool Steel
1.2360 X48CrMoV8-1-1 Cold Work Tool Steel
1.2360 X48CrMoV8-1-1 Cold Work Tool Steel
Model
1.2360 X48CrMoV8-1-1

Item specifics

Delivery Condition
+N or +A or +QT
Surface Condition
black or turned or polished

Review

Description

1.2360 X48CrMoV8-1-1 Cold Work Tool Steel

 

1.2360 X48CrMoV8-1-1 Alloy tool steel with increased chromium content, average strength, high hardness, ductility and high abrasion resistance. Used for precision woodworking tools - knives, blades, cutters, handles for the paper, wood, pulp, and paper industries, as well as cold forming tools. The increased content of vanadium provides a high hardenability, which makes it possible to achieve hardness within the limits of 60 HRC.

 

Applications

Blanking tools, stamping tools, embossing tools, forming dies, press dies, die inserts, extrusion dies, reinforcements, cold extrusion tools, tube tools, cutting tools, industrial knives, wood chipping knives, veneer knives.

 

Chemical composition % of the ladle analysis of grade 1.2360

C()

Si()

Mn()

P()

S()

Cr()

Mo()

V(%)

0.45-0.50

0.70-0.90

0.35-0.45

Max 0.020

Max 0.005

7.30-7.80

1.30-1.50

1.30-1.50

 

Mechanical properties of grade 1.2360

Proof strength
Rp0.2(MPa)

Tensile strength
Rm(MPa)

Impact energy
KV(J)

Elongation at fracture
A(%)

Reduction in cross section on fracture
Z(%)

As-Heat-Treated Condition

Brinell hardness(HBW)

573(≥)

122(≥)

21

22

12

Solution and Aging,Annealing,Ausaging,Q+T,etc

311

 

Mechanical properities and heat treatment of steel 1.2360, X48CrMoV8-1-1:

Hardness in annealed condition <240 HB

Annealing in temperatures 835 - 865℃ cooling with furnace

Stress relief annealing at 650℃ cooling the furnace

Quenching at 1035 - 1070℃ with cooling in oil, salt bath or air

Tempering at temperatures 100 - 600℃