1.2601 X165CrMoV12 Cold Work Tool Steel
1.2601 X165CrMoV12 Cold Work Tool Steel
1.2601 X165CrMoV12 Cold Work Tool Steel
1.2601 X165CrMoV12 Cold Work Tool Steel
1.2601 X165CrMoV12 Cold Work Tool Steel
Model
1.2601 X165CrMoV12

Item specifics

Process
hot rolled or hot forged
Delivery Condtion
annealed
Surface Condition
smooth, bright

Review

Description

1.2601 X165CrMoV12 Cold Work Tool Steel

 

X165CrMoV12 1.2601 is a German Cold work tool alloy steel material grade.it is shock resisting steel. it belong to DIN 17350 standard. Digital Grade material number 1.2601. Metal Steel Grade W-Nr X165CrMoV12  It is a die steel, use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cutting mold.

 

Applications

Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working

rolls , measuring tools .

 

Material equivalent of DIN X165CrMoV12 | 1.2601 steel

Germany

Italy

Sweden

Spain

DIN,WNr

UNI

SS

UNE

X165CrMoV12 | 1.2601

X165CRMOW12KU

2310

X160CRMOV12

 

Chemical composition (wt.%) of 1.2601

C

Si 

Mn 

P

S

Cr

Mo

Other

1.55-1.75

0.25-0.40

0.20-0.40

0.030

0.030

11.0-12.0

0.50-0.70

V   0.10-0.50
W   0.40-0.60

 

Mechanical Properties of 1.2601

Rp0.2 (MPa)

Rm (MPa)

Impact
KV (J)

Elongation
A (%)

A Z (%)

Delivery

Hardness HB

641 (≥)

662 (≥)

23

14

31

Solution & Aging, Ann, Ausaging, Q+T

142

 

Heat treatment of X165CrMoV12 | 1.2601 Cold work tool steel

Annealing: Annealing temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255

Quenching: Hardening temperature/℃: 980~1010, Quenching in oil or air

Tempering: Commonly used drawing temperature/℃: 180~250;  After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58

Normalizingat Normalizing temperature, then cool in furnace